ホウ珪酸ガラス粒子
粒子密度 2.2 g/cc （± 0.1 g/cc）
粒径範囲内の粒子 > 90 %
球状粒子率 > 90 %
屈折率 約1.48
形態 乾燥粒子
| 製品番号 | 粒子密度 | 粒径 | 内容量 |
| BSGMS-2.2 38-45um – 10g | 2.2 g/cc | 38 ～ 45 μm | 10 g |
| BSGMS-2.2 45-53um – 10g | 2.2 g/cc | 45 ～ 53 μm | 10 g |
| BSGMS-2.2 53-63um – 10g | 2.2 g/cc | 53 ～ 63 μm | 10 g |
| BSGMS-2.2 63-75um – 10g | 2.2 g/cc | 63 ～ 75 μm | 10 g |
| BSGMS-2.2 75-90um – 10g | 2.2 g/cc | 75 ～ 90 μm | 10 g |
| BSGMS-2.2 90-106um – 10g | 2.2 g/cc | 90 ～ 106 μm | 10 g |
| BSGMS-2.2 106-125um – 10g | 2.2 g/cc | 106 ～ 125 μm | 10 g |
| BSGMS-2.2 125-150um – 10g | 2.2 g/cc | 125 ～ 150 μm | 10 g |
| BSGMS-2.2 150-180um – 10g | 2.2 g/cc | 150 ～ 180 μm | 10 g |
| BSGMS-2.2 180-212um – 10g | 2.2 g/cc | 180 ～ 212 μm | 10 g |
| BSGMS-2.2 212-250um – 10g | 2.2 g/cc | 212 ～ 250 μm | 10 g |
| BSGMS-2.2 250-300um – 10g | 2.2 g/cc | 250 ～ 300 μm | 10 g |
| BSGMS-2.2 300-355um – 10g | 2.2 g/cc | 300 ～ 355 μm | 10 g |
| BSGMS-2.2 600-710um – 1g | 2.2 g/cc | 600 ～ 710 μm | 1 g |
| BSGMS-2.2 710-850um – 10g | 2.2 g/cc | 710 ～ 850 μm | 10 g |
| BSGMS-2.2 850-1000um – 10g | 2.2 g/cc | 850 ～ 1000 μm | 10 g |
| BSGS-2.2 1.0-1.2mm – 10g | 2.2 g/cc | 1.0 ～ 1.2 mm | 10 g |
| BSGS-2.2 1.2-1.4mm – 10g | 2.2 g/cc | 1.2 ～ 1.4 mm | 10 g |
| BSGS-2.2 1.4-1.7mm – 1g | 2.2 g/cc | 1.4 ～ 1.7 mm | 1 g |
| BSGS-2.2 1.7-2.0mm – 10g | 2.2 g/cc | 1.7 ～ 2.0 mm | 10 g |
| BSGS-2.2 2.0-2.4mm – 10g | 2.2 g/cc | 2.0 ～ 2.4 mm | 10 g |
| BSGS-2.2 3.10-3.15mm – 25g | 2.2 g/cc | 3.10 ～ 3.15 mm | 25 g |
| BSGS-2.2 3.85-4.00mm – 25g | 2.2 g/cc | 3.85 ～ 4.00 mm | 25 g |
| BSGS-2.2 4.80-4.95mm – 25g | 2.2 g/cc | 4.80 ～ 4.95 mm | 25 g |
| BSGS-2.2 5.80-6.15mm – 25g | 2.2 g/cc | 5.80 ～ 6.15 mm | 25 g |